Intumescent for fire and heat protection
Flaton-flex A, our highly flexible intumescent for fire protection. This is a material that does not break even under extreme loads, thus enabling its use even in the case of difficult geometries.
The mode of action is based on the formation of a heat-insulating foam in the event of fire. Joints, gaps and other openings are filled by the foam and prevent the passage of heat in the event of fire.
- halogen-, antimony-, silicone- and solvent-free
Fire-resistant protection in joints, gaps and other openings in components and special components.
Fields of application: doors and gates, flaps/dampers, cabinet and partition walls, safety, data and control cabinets, cable passages, ventilation flaps and other shut-off devices.
| Material thickness | 1,0 mm | 1,5 mm | 2,0 mm |
| Basis weight | 1,1 kg/m² | 1,5 kg/m² | 2,0 kg/m² |
| Expansion start | 150 °C | ||
| Foam factor 30 min. 450 °C with superimposed load | 10 to 19 times | ||
| Inflation pressure at 300 °C | 1,2 - 2,4 N/mm² | 1,4 - 2,5 N/mm² | 1,6 - 2,6 N/mm² |
| Fire behavior | Building material class B2 according to DIN 4102 | ||
| Direction of action | three-dimensional | ||
| Specific resistance | > 108 Ω cm | ||
Due to its composition, Flaton-flex A has clear advantages over the competition in the field of exterior applications.
- resistant to ageing
- water resistant
- UV-resistant
- freeze-thaw cycle resistant
-
FROM150 °CEXPANSION START
-
up to19 facheVOLUME ENLARGEMENT
-
STRIP CUT TO250 cmLENGTH